2025 ALUMINUM COATING USING CARBON POWDER WITH TEMPERATURE OF 600°C, 700°C AND 800°C USING HEAT TREATMENT METHOD
Keywords:
Heat treatment, aluminum, heat, metal platingAbstract
Aluminum coating in Indonesia is one of the business fields that has experienced an increase in development and rapid progress starting from the type of coating used to produce coatings that also vary. The purpose of this study was to determine the hot temperatures of 600°C, 700°C and 800°C in the aluminum coating process uses carbon powder and determines the effective hardness values at temperatures of 600°C, 700°C, and 800°C. Test result hardness shows that the highest average hardness value is at a temperature of 600°C of 68.6 Hv and the lowest average hardness value is at a temperature of 800°C which is equal to 51.7 Hv
References
A. P. J. Permana and B. C. P. Mbulu, "The design of Plasma Reactor and Study of Oxgyen Gas Flow Effect against to the Carbon Ashing Rate in Steel K110," NATURAL B: Journal of Health and Environmental Sciences, vol. 4, no. 4, 2018.
J. P. Mahtani, Optical and Structucal Characterization Of Amorphous Carbon Films, Toronto: Dapertement Of Electrical ang Computer Engineering University, 2010.
B. T. Sofyan, Pengantar Material Teknik, Jakarta: Salemba Teknika, 2011.
A. Haryanto, Pengaruh Variasi Tegangan Listrik pada Proses Anodizing Terhadap Kekerasan Aluminium, Yogyakarta: Universitas Muhammadiyah Yogyakarta, 2017.
M. Nofri, "Analisis Perubahan Sifat Mekanik Aluminium 6063 Setelah Dilakukan Perlakuan Panas Pada Suhu Tetap dengan Waktu Tahan Bervariasi," Bina Teknika, vol. 16, no. 1, pp. 33-42, 2020.
G. E. Dieter, Metalurgi Mekanik, Jakarta: Erlangga, 1987.
T. Surdia and S. Saito, Pengetahuan Bahan Teknik, Jakarta: PT. Pradnya Paramita, 1985.
Junipitoyo, "Pengaruh Variasi Suhu Dan Waktu Heat Treatment Pada Aluminium Alloy 2024-T3 Terhadap Sifat Fisis Dan Mekanis Dengan Media Pendingin Oli," Jurnal Penelitian Politeknik Penerbangan Surabaya, vol. 5, no. 2, 2020.
M. H. A. Hasa, "Pengaruh Temperatur Heat-Treatment terhadap Kekerasan dan Stuktur Mikro Paduan Al-Fe-Ni," Jurnal Rekayasa Proses, vol. 4, no. 2, 2010.
G. Methers, The Welding Of Aluminium and its Alloys, Cambridge: Abington Hall, 2002.